Selection Guide FSH Welding Flux-Cored Wires for build-up and hardfacing Gas shielded for assembling Gas shielded for build-up and hardfacing

Open arc flux-cored wire with a high chromium carbide deposit for hardfacing on carbon, manganese and stainless steels, subjected to severe abrasion with moderate impact.

HARDFACING

Hardness (as welded) = 60 HRC

Drum on request

Spool ø: .045” 1/16” (1.2 mm) (1.6 mm)

Coil ø: 1/16” 3/32” 7/64” (1.6 mm) (2.5 mm) (2.8 mm)

Open arc flux-cored wire containing chromium carbides for economical hard facing on mild, low alloy, and manganese steels subjected to severe abrasion and moderate impact.

HARDFACING

Hardness (as welded) =40-45 HRC Work-hardened = 50-55 HRC

Drum on request

Spool ø: .045” 1/16” (1.2 mm) (1.6 mm)

Coil ø: 3/32” 7/64” (2.5 mm) (2.8 mm)

Open arc flux-cored wire containing uniformly distributed complexes carbides in a hard matrix. Ideal for hardfacing on mild and low alloy steels, stainless steels and manganese steels subjected to severe abrasion, heat and moderate impact.

HARDFACING

Hardness (as welded) = 62-64 HRC

Drum on request

Spool ø: .045” 1/16” (1.2 mm) (1.6 mm)

Coil ø: 3/32” 7/64” (2.5 mm) (2.8 mm)

Open arc flux-cored Cr-Ni-Mn wire for joining and build-up carbon steels, low alloy and 11-14% manganese steels (Hadfield steels). Ideal as a cushion before hardfacing. Excellent resistance to severe impact with moderate abrasion and corrosion.

BUILD-UP

Rm = 125 000 psi (865 MPa) Hardness (as welded) =250 HB Work-hardened = 550 HB

Drum on request

Spool ø: .045” 1/16” (1.2 mm) (1.6 mm)

Coil ø: 1/16” 3/32” 7/64” (1.6 mm) (2.5 mm) (2.8 mm)

Open arc flux-cored wire for economical build up on mild, low alloy and manganese steels. Excellent as a cushion before hard facing. Excellent resistance to severe impact with moderate abrasion.

BUILD-UP

Hardness (as welded) =170-200 HB Work-hardened = 425-480 HB

Drum on request

Spool ø: 1.2 mm 1.6 mm (.045”) (1/16”)

Coil ø: 1.6 mm 2.5 mm 2.8 mm (1/16”) (3/32”) (7/64”)

Open arc flux-cored wire for building up and overlaying before hardfacing on high alloy steels, manganese steels and difficult-to -weld steels. High resistance to severe impact, moderate abrasion, heat and corrosion.

BUILD-UP

Hardness (as welded) =225 HB (Work hardening deposit)

Drum on request

Coil ø: 1/16” 3/32” 7/64” (1.6 mm) (2.5 mm) (2.8 mm)

Spool ø: 1/16” (1.6 mm)

Rm = Tensile strength Re = Yield strength E = Elongation